Austenite/ Martensite/ Ferrite Irregular Stainless Steel Powder for Sintering Parts 005 manufacturer from China Shijiazhuang Daye Metal Powder Factory

Austenite/ Martensite/ Ferrite Irregular Stainless Steel Powder for Sintering Parts

Payment Terms:	T/T,L/C
Place of Origin:	Hebei, China (Mainland)


	Add to My Favorites
HiSupplier Escrow	Share \|

Product Detail

Model No.: 005

Packing: 25kg/iron barrel

Production Capacity: 2500 TON PER YEAR

Delivery Date: 7-15 working days after rec...

Stainless Steel Powder for Sintering Parts

Stainless Steel Powder for Sintering Parts

Product Introduction
We adopted the best refining process to make the ingredients matched and more uniform.
Compressibility,compactibility and green density can achieve the best results in a stable condition on the basis of our rich experience in mixing additives.

Technical Parameters

	Austenitic Stainless Steel						Ferritic Stainless Steel		Ferritc/Martensite Stainless Steel
	304L		303L		316L		409LE	434L	410L
Powder Properties

Apparent Density, g/cm3	2.85		2.90		2.75		2.70	2.72	2.70
Flow Rate, s/50g	28		27		32		34	34	34
Chemical Compositions
C, %	0.02		0.02		0.02		0.02	0.02	0.02
Ni, %	9.5		10.2		12.8
Fe, %	Balance		Balance		Balance		Balance	Balance	Balance
Cr, %	19		19.5		18		12	16.8	12.5
Si, %	0.9		0.9		0.8		0.8	0.8	0.8
O, %	0.2		0.2		0.2		0.2	0.2	0.2
N, %	0.03		0.03		0.03		0.03	0.03	0.03
Mo, %					2.5			1.0
Nb, %							0.5

Sieving (µm )
+150, %	0.8		0.8		1		0.9	0.9	0.9
-45, %	43		40		41		45	42	42

The Green Properties
GD 600 MPa g/cm3 The Green Density with Lubricant	6.45		6.4		6.5		6.45	6.45	6.45
GS 600 MPa, Mpa The Green Strength with Lubricant	7.5		7.1		8.5		14	12	13
Lubricant = 1% Acrawax

Sintering Temperature	1150° C	1250° C	1150° C	1250° C	1150° C	1250° C	1250° C	1250° C	1250° C
Sintering Density, g/cm3	6.7	6.78	6.68	6.75	6.85	6.92	6.9	6.9	7.02

Performance and Application Examples	- Excellent Corrosion Resistance - Non-Magnetic - Application is suitable for the production of locks and home appliance parts.		Free processing of Austenitic Stainless Steel		- Corrosion resistance is extremely high, especialy suitable for chlorine ion solution - Non-Magnetic - Often used in the production of stainless steel powder metallurgy parts in different areas, such as small gear, cam and linker		- Medium Corrosion Resistance - Ferromagnetic - Suitable for welding - Suitable for the production of automobile exhaust flage and hot exhaust gas oxygen sensor hubparts	- Medium Corrosion Resistance and higher than 400 series - Excellent magnetic property - Suitable for the production of automobile exhaust flange parts	- Medium Corrosion Resistance - Ferromagnetism - Suitable for the production of sensor circle parts of ABS system - Graphite can be added ( to increase hardness and abrasion performance) 410/420 Convert into Martensite Stainless Steel 410/420